آماده سازی و خصوصیات نانوکامپوزیت گرافیت گسترش یافته/EPS رسانای الکتریکی
|کد مقاله||سال انتشار||مقاله انگلیسی||ترجمه فارسی||تعداد کلمات|
|57846||2007||7 صفحه PDF||سفارش دهید||محاسبه نشده|
Publisher : Elsevier - Science Direct (الزویر - ساینس دایرکت)
Journal : Composites Science and Technology, Volume 67, Issues 11–12, September 2007, Pages 2528–2534
Nanocomposites based on poly (phenylene sulfide) (PPS) and expanded graphite (EG) or ultrasonicated EG (S-EG) were prepared by melt blending. Morphologies of the nanocomposites were examined using both SEM and TEM. Electrical conductivity and thermal stability of PPS were notably enhanced by the introduction of EG. The percolation threshold values are 1 wt% (S-EG) and 2 wt% (EG) for PPS/S-EG and PPS/EG nanocomposites, respectively. The variation of mechanical strength with the weight fraction of EG and S-EG in the nanocomposites showed somewhat correlation with the threshold filler concentration. The crystallization behavior of PPS matrix in the nanocomposites was investigated using DSC, and the results indicated that the crystallization process was significantly accelerated, leading to an increase in crystallinity.