تأثیر سری آلکاندیول به عنوان افزودنی های فرآوری شده در لایه فعال عکس بر روی بازده تبدیل انرژی سلول های خورشیدی پلیمری
|کد مقاله||سال انتشار||تعداد صفحات مقاله انگلیسی||ترجمه فارسی|
|54228||2013||7 صفحه PDF||سفارش دهید|
Publisher : Elsevier - Science Direct (الزویر - ساینس دایرکت)
Journal : Solar Energy Materials and Solar Cells, Volume 114, July 2013, Pages 82–88
The alkanediol series such as 1,2-ethanediol, 1,3-propanediol, 1,4-butanediol, 1,6-hexanediol, 1,8-octanediol and 1,10-decanediol was introduced to poly(3-hexylthiophene, P3HT):[6,6]-phenyl-C61-butyric acid methyl ester (PCBM) based bulk-heterojunction (BHJ) polymer solar cells as processing additives. When 1,3-propanediol was introduced to photo-active layer as a processing additive, power conversion efficiency (PCE) was dramatically increased from 3.5% (for the reference device) to 5.3%. To investigate the causes of improvement of the PCE of PSCs after addition of alkanediol series, photon absorbance properties were observed using UV–vis spectroscopy and photoluminescence (PL). Then, the degree of crystallinity of P3HT was examined through X-ray analysis. In addition, changes in the nano-structure and surface morphology of P3HT:PCBM blend film were observed through AFM and TEM. The series resistance (RS) of the fabricated PSCs was 5.19 Ω cm2, and short circuit current density (JSC), open circuit voltage (VOC) and fill factor (FF) were 16.2 mA/cm2, 0.63 V and 51.9% respectively.