Because tungsten (W) is used in present fusion devices and it is a reference material for ITER divertor and possible plasma-facing material for DEMO, we strive to understand the response of different W grades to ion bombardment. In this study, we investigated the behavior of mirrors made of four polycrystalline W grades under long-term ion sputtering. Argon (Ar) and deuterium (D) ions extracted from a plasma were used to investigate the effect of projectile mass on surface modification. Depending on the ion fluence, the reflectance measured at normal incidence was very different for different W grades. The lowest degradation rate of the reflectance was measured for the mirror made of recrystallized W. The highest degradation rate was found for one of the ITER-grade W samples. Pre-irradiation of a mirror with 20-MeV W6+ ions, as simulation of neutron irradiation in ITER, had no noticeable influence on reflectance degradation under sputtering with either Ar or D ions.